Supplying high temperature epoxy flake clay _ precautions, Tel: 15230673339 Liu, national free hotline: 400-621-3026 clay glass flake coatings can prevent water vapor and chemical solvents on the base material erosion. The extent of the substrate or coating with chemical resistance of the glass material chosen varies, organized by C- glass into glass flakes having excellent chemical durability. Since the relative and steel, cement and other base material larger coefficient of elongation, so in the case of thermal shock and cracking of the resin layer is likely to fall off, and the glass flakes to provide a thermally stable layer, which can prevent cracking of the substrate and off good heat resistance. Shall be subject to the use of the glass flakes before coupling treatment, in order to increase the adhesive force between the flake and the resin in the resin and are arranged in parallel, and the floating stability in the coating system, thereby increasing the permeability of the coating. Coupling can choose a silane coupling agent or titanate coupling agent, coupling different resins should be selected and the corresponding treatment process looks different molecular structure. As clay, glass flakes can be used when a primer about 30 mesh, glass flake size and have a direct impact on the amount of coating performance. Using smear method and roll coating method of construction is good; when making paint, use a 200-mesh glass flakes, spraying construction method is more appropriate than the commonly used Graco airless sprayer and Hotsprai thermal sprayer. Scales clay, clay flake anti-corrosion materials, scales scaly clay clay operators where to buy glass flake clay Features: ※ with impermeability, frost, salt, alkali resistance, weak acid corrosion resistance, and bonded with a variety of materials very strong. ※ thermal expansion coefficient close to the concrete, it is difficult to disengage from these substrates to be bonded and durability. ※ construction in the wet surface of the substrate, without drying, can harden in wet conditions or underwater. ※ non-flammable, non-explosive, do not pollute the environment, harmless to human health. ※ low cost, only 30-50% of epoxy resin mortar. ※ construction easy to operate, with ordinary cement mortar construction, easy to clean, it can be cleaned with water. Physical performance indicators: Test items Performance test results flexural strength (Mpa) 28d6.06.49 compressive strength (Mpa) 7d ---- ≥2528d> 20≥35 neutral resistance (mm) 28d <5.01.8 stick knot strength (Mpa) at room temperature normal 28d> 1.02.8 thermal cycling 28d> 1.02.4 permeable amount (g) <201524h water absorption (g / m3) <1000525 absorption coefficient (kg / cm2 · h0.5) <0.50. 32 Usage: ☆ check the product packaging intact, check the label is correct. ☆ open the lid, the bucket 3 bags marked with pre ingredients A, B, C are removed. ☆ A material, B material after shaking, were poured into the bucket and stir evenly, then marked with a "C", slowly stirring the powder into the barrel, mixing mortar into a uniform shape can be. If more viscous or difficult to stir, this package can be added to 1-2kg of clean water and stir, does not affect the final performance of the product mixture. Supplying high temperature epoxy flake clay _ Note Currently, glass flake clay has become FGD (FGD) technology of choice for anti-corrosion, commonly used in the United States and Japan, the introduction of devices now running our country are using this technique, it is just as mentioned above, due to the scale clay VEGF has good permeability, small construction difficulty, easy to repair less physical failure and moderate cost and other advantages. Thus, VEGF scaly clay is widely used in electric power, metallurgy and chemical industry, especially in the power system flue gas desulfurization (FGD) systems. Glass flake coatings on a variety of anti-infiltration capacity of the medium is much higher than fiberglass, such as chemical mediators, gas and steam, and other media, are difficult to penetrate the glass flake coatings, glass flake paint coating production rarely occur water vapor diffusion. Glass flake coatings have this characteristic of the reason is that the laminated glass flakes arranged in resin. Supplying high temperature epoxy flake epoxy clay _ Caution temperature scales clay dealers, high temperature epoxy clay manufacturers flake epoxy flake mortar construction team acid salt and sea, ⑹ scaffolding scaffold board work surface should be paved. Coupled with a staggered arrangement of the upper and lower coating has excellent resistance to medium permeability and corrosion resistance, the scope of ice and 1 hour