Glass flake epoxy glass flake epoxy primer clay, Tel: 15230673339 Liu, nationwide toll-free hotline: 400-621-3026 vinyl coating on a glass flake concrete base using: glass flake clay by hand trowel scraping trowel into 1-2mm (per channel) VEGF thick clay layer, after hardening, then a second Daogua trowel until the required thickness. Typically 1mm thickness at each coating is detected in order to confirm whether there are pinholes and other coating defects. ③ convex parts, appropriately increased thickness, or use of FRP composites. ④ with VEGF resin Overlay one to two. Glass flake clay foundation concrete conservation of not less than 28 days, the surface moisture content should be <6%. First, the surface and remove alkaline substances, and after the use of sandblasting or other mechanical means to remove the concrete surface floating dust, clean up after, and then with VEGF resin bottoming one to two, to be dry construction. Glass flake paint simple construction, can brush, roller and airless spray painted. Surface treatment must be carried out before painting, de-rust after degreasing and roughened by blasting, shot peening. After 4 usually 20-40 mesh sand or quartz sand to 5-7kg / cm2 compressed air driven sand and grit to 50 ~ 70m / s velocity ejected from the nozzle, the surface of SIS Sa2.5 specifications, clear sandblasting dust, paint over 8h hours. Painting is generally carried out in dry weather, temperature above 5 ℃, relative humidity below 85%. With the same kind of resin or glass flake (smaller particle size) as a primer, having a thickness of 50 microns, after finger touch dry primer coated glass flake coating. Glass flake paint, glass flake paint much money, glass flake paint clay construction program scales manufacturer of glass flake clay coating prevents water vapor and chemical solvents on the base material erosion. The extent of the substrate or coating with chemical resistance of the glass material chosen varies, organized by C- glass into glass flakes having excellent chemical durability. Since the relative and steel, cement and other base material larger coefficient of elongation, so in the case of thermal shock and cracking of the resin layer is likely to fall off, and the glass flakes to provide a thermally stable layer, which can prevent cracking of the substrate and off good heat resistance. Glass flake epoxy glass flake epoxy primer clay glass flake epoxy anti-corrosion coatings applied to steel pipes buried and underwater and all kinds of steel corrosion, is used to prevent leakage of various concrete structures and as a wear-resistant, slip layer. Also applies to steel oil, water, gas tanks and chemical containers inside and outside the walls of corrosion, coal tar epoxy glass flake coating for containing coal tar, black, applies only to crude oil, heavy oil, sewage, gas tanks and chemical containers outer wall corrosion, does not apply to light-colored petroleum products, solvents and benzene in drinking water tank wall corrosion. At home and abroad of FGD solvent-free epoxy glass flake anti-corrosion coating applied to a variety of long-term corrosion protection of steel or concrete harsh corrosive environments, such as underground water, sewage tank and in contact with the substrate, and so some chemical mediators device selection mainly nickel-based corrosion resistant alloy; rubber lining, especially soft rubber lining; synthetic resin coating, especially resin with glass flakes; fiberglass; corrosion resistant plastics such as polytetrafluoroethylene; impervious graphite; silicate materials such as chemical corrosion ceramics; artificial cast stone and so on. Glass flake epoxy glass flake epoxy primer clay glass flake paint operation, glass flake paint construction technology, glass flake epoxy primer dealers comply with environmental protection requirements, were discussed on the corrosion mechanism and glass flakes pointed out that the selection and good surface treatment of glass flake coatings class is the key to get good performance, Al2O3F, although glass flakes in the resin matrix continuous phase is nearly parallel arrangement, sulfur dioxide emissions for 900-1500 tons,